Polyimide Film 6051 Standard No: JB/T2726-1996 Application scope: The polyimide film is produced by adopting ”Doctor-Blading Process”.It processes heat-resistant, radiation resistant and excellent dielectric performance and applies to motor grade H electrical insulation as well as the electric engineering insulating materials for other usage. Technical specifications.

1. Appearance: Film surface is smooth, bright and clean. It shall have no defects, such as folding, tearing, particulate air bubble, pinhole, and any external impurity. Its edges shall be tidy and have no breakage. And the film is provided in rolls.

2. Dimension 1) Thickness and acceptable tolerance: see the recommended thickness in Table One. The products with other thickness can be supplied according to the requirements of customer.

Table One:

Thickness,um

     25

      4

     50

      75

     100

Tolerance,um

     +4

     +6

     +7

      +8

     +10

     -3

     -5

     -6

      -6

      -7

2) Width: no less than 250mm, acceptable tolerance is +-1.6mm. Other tapes with different width can be supplied according to the customer’s requirement. 3) Length: according to the customer’s requirements. 3. General properties: (showed in Table Two)

Table Two:

No.

Index Description

  Unit

                    Index Value

  25μm

  40μm

  50μm

  75μm

  100μm

1

Density

kg/m3

                 1.420*10 ±0.02

2

Tensile Strength

         MD

  Mpa

                 ≥135

         TD

                 ≥115

3

Elongation at break

         MD

   %

                 ≥35

         TD

4

Shrinkage,MD and TD

   %

 

                  150℃

                 ≤1.0

                  400℃

                 ≤3.0

5

Dielectric Strength

       Average

 MV/m

          ≥150

 ≥130

  ≥110

      Individual

          ≥100

 ≥80

  ≥70

6

Surface resistivity  At 200℃

   Ω

                 ≥1.0*1015

7

Volume resistivity  At 200℃

  Ω.m

                 ≥1.0*1013

8

Relative dielectric constant 48-62Hz

   —

                       3.5±0.4

9

Dielectric loss factor 48-62Hz

   —

                ≤4.0*10-3

10

Long-term thermal resistance index

   —

                ≥180