Phenolic cotton cloth laminate sheet is made of cotton cloth impregnated with phenolic resin after drying and hot pressing.
Type: PFCP201 PFCP202 PFCP203 PFCP204 PFCP206 PFCP207 
Features:
1.Normal Dimension:1020mmx1220mm, 1020mmx2040mm, 1220mmx2470mm
2.Normal Thickness:0.5mm to 50mm
Advantage:
With electrical properties and good mechanical properties under normal conditions.
Applications :
1.PFCP201:Primarily intend for mechanical application, with better strength than other types of PFCP.
2.PFCP206:Suitable for mechanical & electrical application, with good electrical properties under high humidity conditions, this grade may be punched hot.
3.PFCP207:Similar in mechanical performance to PFCP201, with better punching practice at lower temperatures than PFCP201.
Phenolic cotton cloth laminate sheet is made of cotton cloth impregnated with phenolic resin after drying and hot pressing.
Type: PFCP201 PFCP202 PFCP203 PFCP204 PFCP206 PFCP207 
Features:
1.Normal Dimension:1020mmx1220mm, 1020mmx2040mm, 1220mmx2470mm
2.Normal Thickness:0.5mm to 50mm
Advantage:
With electrical properties and good mechanical properties under normal conditions.
Applications:
1.PFCP201:Primarily intend for mechanical application, with better strength than other types of PFCP.
2.PFCP206:Suitable for mechanical & electrical application, with good electrical properties under high humidity conditions, this grade may be punched hot.
3.PFCP207:Similar in mechanical performance to PFCP201, with better punching practice at lower temperatures than PFCP201.

  Properties 

     Units

    PFCC201

  PFCC202

   PFCC203

    PFCC204

Flexural strength perpendicular to lamination      ≥

      MPa

        100

       90

       110

        100

Notch impact strength parallel to lamination charpy        ≥

     KJ/m2

        8.8

       7.8

        7.0

         6.0

Bonding strength   ≥

       N

         —

        —

         —

       —

Dielectric strength perpendicular to lamination 
(in oil 90±2℃)  ≥

    MV/m

       0.82

       5.1

       0.82

         6.3

Breakdowm voltage parallel to lamination
(in oil 90±2℃) ≥

       KV

          1

       20

         1

          20

                           Dielectric strength

Relative dielectric coefficient    ≤

       —

         —

       5.5

        —

         5.5

Insulation resistance after impregnated in water        ≥

       Ω

      1×106

      5×107

      1×106

       5×107

Water absorption
1mm         ≤

       mg

        206

       136

        206

         136

Colour

        —

                              Natural or black

Reference standard

        —

                              JB/T8149.2-20

You are warmly welcome to raise your special requirement, so as to make design and studies in special in order to produce more qualified new type laminated sheet.